ASTM D(). Standard Test Method for Coating Flexibility of Prepainted Sheet. standard by ASTM International, 09/01/ View all product details. Standard Test Method for Coating Flexibility of Prepainted Sheet – ASTM D . Hide. Search. Start. Standard ASTM standard · ASTM D This professional T-Bend Tester is designed and engineered in accordance with international test standard, e.g. ASTM D (Standard Test Method for.
|Genre:||Health and Food|
|Published (Last):||23 November 2011|
|PDF File Size:||14.7 Mb|
|ePub File Size:||7.83 Mb|
|Price:||Free* [*Free Regsitration Required]|
ASTM D The “T”-bend test is a very important test for ensuring asmt adhesion of the paint film during critical bending of the metal sheet.
Prepainted Steel Test Archives – UNICOIL
Pencil Hardness Test Standard: This test involves dropping a mass of about 2 kg from a height of about 70 cm, thereby exerting a falling force of 13 Joules. Surface gloss relates to the light reflectance from a painted surface. Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM Headquarters.
It is the responsibility of the user of this standard to establish appro- priate safety and health practices and determine the applica- bility of regulatory wstm prior to use. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk of d44145 of such rights, are entirely their own responsibility.
A noncured paint film has a lower pencil hardness, which makes it more likely to be damaged. The bend direction, whether the axis of bend is transverse to or along the rolling direction of the metal, and the temperature of the specimen when it is bent can affect the results of this test and should be agreed upon between the supplier and the user.
A number in parentheses indicates the year of last reapproval. This test is a means of 3. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. The gloss levels include low gloss, medium gloss, and high gloss. The associated energy transfer will result in loosening of the paint film.
The “T”-bend test is a very important test for ensuring the adhesion of the paint film during critical bending of the metal sheet. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. This test is performed using the organic solvent methyl ethyl ketone. These stresses can exceed the flexibility or adhesive strength of the coating, resulting in fracture of the coating which exposes the substrate, or in the loss of adhesion of the coating to the substrate.
A greater solvent resistance indicates that the paint film is more stable and durable for outdoor exposure. The elasticity is measured with the aid of an eye piece after magnifying an image of the paint surface. Standard samples and the test sample are positioned side by side and analyzed for shade variations.
A superscript epsilon indicates an editorial change since the last revision or reapproval.
The values given in parentheses are for information only. A “0” T bend is the most critical and 5 T is less critical.
Standard Test Method for Coating Flexibility of Prepainted Sheet
Organic coatings on precoated sheet are subjected to stresses when fabricated into products by roll forming, brake bending, or other deformation processes. Elasticity refers to the flexibility of the paint film when the metal sheet is subjected to radius bending. Continue to bend the free end around the testing. This is an accelerated corrosion test for organic coatings.
A bench vise with smooth stresses when fabricated into products by roll forming, brake jaws or with smooth inserts, preferably of a soft metal to avoid bending, or other deformation processes. Reverse Impact Test Standard: Examine the tape for coating removed from the surface of the specimen that is, pickoff. The solvent resistance test indicates the stability of a paint film exposed to organic solvents.
Standard – Standard Test Method for Coating Flexibility of Prepainted Sheet ASTM D –
The force will vary according to the thickness of the sheet. This is a very important color assessment test. The reverse impact test is a destructive test. The results of this test indicates the degree of curing of the paint film. A 2 by 6-in.
The paint film should not crack while bending the metal.